CHEMICAL COMPOSITION
Silicon Diox ide (SiO2)  >20

Aluminium Oxide (Al2O3) <6.8
Ferric Oxide (Fe2O3) <6

Calcium Oxide (CaO) <66
Magnesium Oxide (MgO%) <6

Sulphur Trioxide (SO3),<3.0
Loss Of Ignition (LOI) < 3.0

Insoluble Residue % <1.3
Tricalcium Silicate (C3S%) <60

Dicalcium Silicate (C2S%) <25

Tricalcium Aluminate (C3A%) <8

Tricalcium Alumino Ferrice (C4AF%) <12

PHYSICAL AND MECHANICAL PROPERTIES
Blain CM2/GR 3.250
Autoclave Expantion 0.02

Normal Consistency % 27.5
Initial Setting Time (Hours:Mins) 3.25 – 4.50
Hard Set (Hours:Mins) 4.54 – 6.00

Fitnes Index (CM2/GM) 2800-3040

COMPRESSIVE STRENGTH

@ 03 DAYS 2.65 – 34.2 KG/CM2

@ 07 DAYS 37.3 – 42.5 KG/CM2

@ 28 DAYS 52.8 – 54.6 KG/CM2